EN 10216-2 Tubo de acero sin costura

Grado de acero

C

Si

Minnesota

P

S

cr

Mes

Ni

Alabama_nene

Cu

ti máximo

nombre de acero

Número de acero

máximo

máximo

P195GH

1.0348

=0.13

=0.35

=0.70

0.025

0.020

=0.30

=0.08

=0.30

=0.020

=0.30

0.040

P235GH

1.0345

=0.16

=0.35

=1.20

0.025

0.020

=0.30

=0.08

=0.30

=0.020

=0.30

0.040

P265GH

1.0425

=0.20

=0.40

=1.40

0.025

0.020

=0.30

=0.08

=0.30

=0.020

=0.30

0.040

16Mo3

1.5415

0.12-0.20

0.40-0.90

0.40-0.90

0.025

0.020

=0.30

0.25-0.35

=0.30

=0.040

=0.30

14MoV6-3

1.7715

0.10-0.15

0.15-0.35

0.40-0.70

0.025

0.020

0.30-0.60

0.40-0.50

=0.30

=0.040

=0.30

13CrMo4-5

1.7335

0.10-0.17

=0.15

0.40-0.70

0.025

0.020

0.70-1.15

0.40-0.60

=0.30

=0.040

=0.30

10CrMo9-10

1.7380

0.08-0.14

0.08-0.14

0.30-0.70

0.025

0.020

2.00-2.50

0.90-1.10

=0.30

=0.040

=0.30

25CrMo4

1.7218

0.22-0.29

0.22-0.29

0.60-0.90

0.025

0.020

0.90-1.20

0.15-0.30

=0.30

=0.040

=0.30

15NiCuMoNb5-6-4

1.6368

=0.17

=0.17

0.80-1.20

0.025

0.020

=0.30

0.25-0.50

1.00-1.30

=0.050

0.50-0.80

X10CrMoVNb9-1

1.4903

0.08-0.12

0.08-0.12

0.30-0.60

0.025

0.020

8.00-9.50

0.85-1.05

=0.40

=0.040

=0.30

a No se agregarán intencionalmente al acero elementos no incluidos en esta Tabla sin el acuerdo del comprador, excepto los elementos que puedan agregarse para terminar el molde. Se tomarán todas las medidas apropiadas para evitar la adición de elementos indeseables procedentes de chatarra u otros materiales utilizados en el proceso de fabricación del acero.

b Este requisito no es aplicable siempre que el acero contenga una cantidad suficiente de otros elementos fijadores de nitrógeno que deberán declararse. Cuando se utilice titanio, el productor deberá verificar que (Al+Ti/2)=0,020%

c Opción 2: Para facilitar las operaciones de conformado posteriores, se aplicará un contenido máximo de cobre acordado inferior al indicado y un contenido máximo de estaño especificado acordado

d No es necesario informar el contenido de estos elementos a menos que se agreguen intencionalmente al elenco.

e Para un espesor de pared de =30 mm, el contenido de carbono se puede aumentar en un 0,02 % para el análisis del producto y del molde.

f No se deberá exceder el valor superior de carbono del 0,23 % para el análisis del producto.

Grado de acero

Propiedades de tracción a temperatura ambiente.

Propiedades de impacto ab

nombre de acero

Número de acero

Límite elástico superior o límite elástico ReH o Rp0,2 para espesor de pared T mín.

De tensión

Fortaleza

habitación

Alargamiento

Un mínimo. % a

Energía mínima absorbida promedio KV J a una temperatura de grado

T Menor o igual a 16

160

40

60

l

t

l

t

MPa

MPa

MPa

MPa

MPa

20

0

-10

20

0

P195GH

1.0348

195

320-440

27

25

40 c

28 d

27c

P235GH

1.0345

235

225

215

360-500

25

23

40 c

28 d

27c

P265GH

1.0425

265

255

245

410-570

23

21

40 c

2s d

27C

16Mo3

1.5415

280

270

260

450-600

22

20

40 c

27 c

14MoV6-3

1.7715

320

320

310

460-610

20

18

40 c f

27 c

13CrMo4-5

1.7335

290

290

280

440-590

22

20

40 c

27 c

10CrMo9-10

1.7380

280

280

270

480-630

22

20

40 c

27 c

25CrMo4

1.7218

345

345

345

540-690

18

15

40 c f

27 c

15NiCuMoNb5-6-4

1.6368

440

440

440

440e

610-780

19

17

40 c f

27 c

X10CrMoVNb9-1

1.4903

450

450

450

450

630-830

19

17

40 c f

27 c

a I=longitudinal t=transversal

b A verificar cuando se especifiquen las opciones 4 y/o 5, a menos que se aplique la nota f)

c Opción 4: Se verificará la energía de impacto.

d Opción 5: Se verificará la energía del impacto longitudinal.

e Para espesor de pared 60 mm< T =80mm

f Ensayo de impacto obligatorio para espesores de pared T =16mm

Grado de acero

Tratamiento térmico un

austenizar

templado

nombre de acero

Número de acero

Grado de temperatura

Medio de enfriamiento

Grado de temperatura

Medio de enfriamiento

P195GH

1.0348

+N b

880 a 940

Aire

-

-

P235GH

1.0345

+N b

880 a 940

Aire

-

-

P265GH

1.0425

+N b

880 a 940

Aire

-

-

16Mo3

1.5415

+N b

890 a 950

Aire

-

-

14MoV6-3

1.7715

+NT antes de Cristo

930 a 990

Aire

680 a 730

aire

13CrMo4-5

1.7335

+NT antes de Cristo

900 a 960

Aire

660 a 730

aire

10CrMo9-10

1.738

+NT antes de Cristo

900 a 960

Aire

680 a 750

aire

25CrMo4

1.7218

+QT

860 a 900

Aire o Líquido

620 a 680

aire

15NiCuMoNb5-6-4

1.6368

+NT c

880 a 980

Aire

580 a 680

aire

X10CrMoVNb9-1

1.4903

+NT c

1040 a 1090

aire

730 a 780

aire

a +N=Normalización, +NT=Normalización + Revenido, +QT=Templado + Revenido (aire o líquido), +I=Recocido isotérmico.

b Normalizar incluye Normalizar la formación.

c For these steel grades it may be necessary in the case of wall thickness T above 25 mm or T/D >0,15 para aplicar temple y revenido con el fin de lograr la estructura y las propiedades del material deseadas. La decisión quedará a criterio del fabricante pero se comunicará al cliente en el momento de la consulta y el pedido. Los tubos de acero tratados de esta manera se designarán con la denominación del acero complementada con el símbolo +QT.